Amalgamation gold recovery time depends on the shape of native gold particle size, the fineness of the gold particles, the mass of mercury, the temperature of amalgamation, pulp density, methods and equipment amalgamation factors. The particle size shape and monomer dissociation degree of gold are mainly related to the grinding operation, especially the influence of monomer dissociation degree. Appropriately improving the fineness of grinding can improve the recovery rate of amalgamation, and it is suitable for gold particles mixed with mercury. The 0.2-0.3 mm, the lower limit of the particle size of the mercury-mixed plate in the grinding cycle is 0.015 mm, but the fine gold particles are lost with the slurry. The color of gold is higher than that of pulse gold. The gold color in the oxidation zone is higher than that of the original ore. The gold with high color is easy to mix with mercury. The amalgamation ability of the gold particle surface is significantly reduced. Mercury is divided into internal amalgamated mercury and externally mixed mercury. The externally mixed mercury is a process of mixing mercury and gold in addition to the grinding operation. Externally mixed mercury is commonly used in domestic fixed mercury amalgamation plates and vibrating amalgamation plates; internal amalgamation is a process of amalgamation and gold extraction in the grinding operation cycle. Gold mines in South Africa and the United States often carry out internal amalgamation in the mining machine. The small and medium-sized gold mines in the former Soviet Union often use the smashing machine, and the common mercury tank is often used in China. Internally mixed mercury is more efficient than externally mixed mercury, and the quality of mercury is good. The concentration of the externally mixed mercury slurry should not be too large to form a loose thin slurry flow, and the flow rate should not be too high, so that the gold particles settle to the mercury plate. The concentration of the internal mixed mercury slurry is preferably 30% to 50%, and the mercury should be suspended. The pH of the slurry has a great influence on the mercury mixing effect. The effect of mixing mercury in the acidic medium and the cyanide solution is good, but in the case of a lot of slime, the acidic medium can not coagulate the slime, and the slime contaminates the surface of the gold particles, affecting the effect of mercury mixing. Mercury is mixed in an alkaline medium, such as the use of lime as a conditioning agent to precipitate soluble salts and eliminate the adverse effects of oil quality. When the pH is between 8 and 8.5, the effect of amalgamation is better. The quality of mercury has a great influence on the effect of mercury amalgamation. Pure mercury is not good for the wetting of gold. Mercury contains a small amount of gold, silver and bismuth metal to reduce the surface tension of mercury and improve the wetting effect. Oil and other organics can contaminate soil and fine gold particle surface, ore sulfide ore, talc, graphite, arsenic compounds easily attached to the surface of the mercury, mercury also affects wetting ability of gold. When adding mercury, the amount of mercury should be increased. Too much will reduce the elasticity and consistency of the mercury paste, so that the mercury paste will be lost with the slurry. Insufficient mercury addition makes the mercury paste hard, loses its elasticity, and reduces the gold-trapping performance. After the mercury plate is put into production, the initial mercury application amount is 15-30 g/m2. After 6-12 hours, mercury is added. The mercury addition amount is 2-5 times of the ore content, and the mercury consumption is usually 3-8. Grams per ton of ore. In addition, the temperature also affects the amalgamation effect. Too low a temperature will increase the viscosity of mercury and affect the effect of mercury mixing. If the temperature is too high, the mobility of mercury will increase, and part of the mercury will be lost with the loss of mercury. Therefore, the mercury-mixing index is prone to seasonal changes, and the mixed temperature should generally be greater than 15 °C. The effect of adding mercury and adjusting the concentration of the slurry is used to eliminate the influence of temperature. Cf30 Peek Rod,Peek Cf 30 Round Bar,Plastic Peek Gf30 Rod,Cf30 Black Round Peek Rod Ningbo Zero Engineering Plastics Co.,Ltd , https://www.zero-peek.com